Common Trade
Name |
304 High Carbon |
|
Material Grade |
304H |
|
UNS |
S30403 |
|
Specification |
ASTM A479 |
|
Approx. Room
Temp. Mechanicals |
"T = 75 ksi, Y =
30 ksi" |
|
Typical % Composition
Summary |
"Cr 18, Ni 8.0 -
10.5, C .04 - .10" |
|
Applications |
"Used primarily
when material is subjected to extreme
temperatures. The high carbon helps
retain strength at the elevated
temperatures." |
|
Corrosion Resistance |
"Austenitic Cr -
Ni stainless. Better corrosion resistance
than 302. Essentially non-magnetic,
becomes slightly magnetic when cold
worked. Lower carbon content means
less carbide precipitation in the
heat-effected zone during welding
and a lower susceptibility to intergranular
corrosion." |